NKG.V · 2019-04-17 12:00:00

Victory Metals Demonstrates Over 90% Vanadium Recovery Using a Hydrometallurgical Leach Process at the Iron Point Project, Nevada

Metallurgy & Processing

Victory Metals Demonstrates Over 90% Vanadium Recovery Using a

Hydrometallurgical Leach Process at the Iron Point Project, Nevada

VANCOUVER

April 17, 2019

/CNW/ -

Victory Metals

TSX-V:VMX

") ("

Victory

" or the "

Company

") is pleased to announce results from initial metallurgical tests

conducted by McClelland Laboratories, Inc. ("

McClelland Laboratories

") of

Sparks, Nevada

, on drill cuttings from the Company's Iron Point Vanadium Project.

Test work using hydrometallurgical processes at atmospheric pressure has yielded vanadium recoveries in excess of 90% in leach times of less than eight hours.

Highlights – Phase I Metallurgical Testwork

Initial bench-scale hydrometallurgical leach testing on Iron Point RC drill cuttings demonstrate up to 94.3% vanadium recovery at atmospheric pressure and 8-

hour leach times

RC drill cutting Master Composite used in testing had a median head grade of 0.38% V

16 preliminary tests were completed utilizing the Master Composite and varying four test factors: temperature, slurry solids density, and concentrations of

hydrofluoric and sulphuric acid

Phase II testing is underway that will further define operating parameters required to develop an economic atmospheric leaching process for Iron Point

vanadium mineralization

Jeff Woods

, Victory's Chief Metallurgist stated: "Preliminary testing last year by McClelland Laboratories on drill core samples indicated that a low-cost

atmospheric leach may be suitable for Iron Point vanadium mineralization. A review of published work led to the first phase of experimental tests released today

utilizing RC drill cuttings. Our preliminary tests confirm that an atmospheric leach process can successfully recover vanadium at levels greater than 90% with

potential for relatively low acid consumption. We are in the process of augmenting the initial test work to optimize recovery and minimize operating costs, before

starting variability testing and solvent extraction/precipitation testing."

Paul Matysek

, Executive Chairman, stated: "Initial metallurgical testing conducted at McClelland Laboratories is very encouraging, creating a pathway forward to

a potentially economic processing route for the Iron Point Vanadium Project. Importantly, the methods explored are done at ambient pressure without the use of

costly pressure oxidization or roasting. Furthermore, these hydrometallurgical methods are commonly utilized in base metal processes and show promise for

applicability to vanadium recovery. Our maiden drilling campaign clearly outlined a large mineralized system. With promising initial metallurgical results returned to

date, we can work towards identifying an economic process that will allow us to fast track towards resource definition and a Preliminary Economic Assessment."

Phase I Testwork

A total of 197 Reverse Circulation ("

") drill reject samples were delivered to McClelland Laboratories of

Sparks, Nevada

, for sample prep, assaying, and

compositing. McClelland Laboratories, established in 1986, is recognized as a top mineral-processing laboratory with a focus on hydrometallurgical extraction of

precious and base metals, as well as specific experience in vanadium metallurgy. Their experience and knowledge have accelerated the development of Victory's

atmospheric hydrometallurgical process.

A Master Composite sample was constructed using 197 drill cuttings interval samples that best represented both the spatial and stratigraphic distribution of

mineralized zones throughout the Iron Point Project as described in Table 1 and shown in Figure 1. Specifically, the Master Composite is made up of cuttings from

drill intervals ranging between a depth of

1.5 m

164.6 m

. Intervals incorporated into the composite had a minimum grade of 0.17% V

, a maximum grade of

1.14% V

, a median grade of 0.38% V

, and a mean (unweighted) grade of 0.34% V

from triplicate analysis.

Table 1: RC Drill Cutting Intervals used in the Master Composite

Number

Range of Depth m

RC Hole ID

Min

Max

Min

Max

Mean

VM-2

9.1

164.6

0.21

0.79

0.45

VM-7

6.1

137.2

0.20

0.79

0.46

VM-18

4.6

65.5

0.21

0.64

0.38

VM-23

1.5

85.3

0.25

0.99

0.61

VM-33

42.7

128.0

0.21

0.71

0.35

VM-76

6.1

146.3

0.17

1.14

0.42

Figure 1: Hole Locations for RC Drill Cutting Intervals used in the Master Composite (CNW Group/Victory Metals Inc)

After a review of published work and some early test work on drill core samples, a Design of Experiments program (DOE) was initiated as a scoping level trial

using four primary leaching factors, namely: leach temperature, slurry solids density, hydrofluoric acid dosage and sulfuric acid dosage. DOE methods are used to

determine the effects of several factors at once and are statistically analyzed to determine the effects of each factors, i.e. acid dosage or temperature, also the

interaction of two or more factors on the system, i.e. temperature and slurry solids density. Owing to the number of factors, a two-level factorial design was used

for the initial runs. Sixteen tests were run using different combinations of Hi and Lo values for each of the factors. All tests were run at atmospheric pressure with

a leach time of eight hours. Initial factor high and low levels were selected based on similar unit operations currently used in the industry, i.e. slurry solids density

20 to 50 percent, which is common in flotation concentrate products and gold leach circuits, respectively. Owing to the atmospheric leaching process, maximum

temperature considered was 100 degrees centigrade. Intermittent samples were taken at two, four, and six hours and each solution analyzed for pH, oxidation-

reduction potential (ORP), and acid concentration. For each test make-up, water and reagents were added as required to maintain the DOE factor levels. At the

termination of the test, samples were filtered with dried solids and leach solutions submitted for analyses. Statistical analysis of the data was done using Stat-

Ease's Design Expert and SAS' JMP statistical analysis software.

Table 2: DOE Parameter Matrix with Summary Agitation Leach Test Results, Iron Point Master

Composite, for each of the 16 Tests

Test ID

Factor 1

Temp.,

Factor 2

Density,

% solids

Factor 3

g/L

Factor 4

g/L

Leach

Time, hr

Recovery,

H2SO4

Consumption

kg/mt

DOE-1

47.3

115

DOE-2

48.9

189

DOE-3

21.3

103

DOE-4

53.5

170

DOE-5

33.7

122

DOE-6

33.0

DOE-7

44.0

102

DOE-8

65.7

N/A*

DOE-9

90.6

142

DOE-10

89.0

103

DOE-11

41.8

118

DOE-12

92.8

DOE-13

66.9

127

DOE-14

71.5

112

DOE-15

75.3

127

DOE-16

94.3

101

Conditions for DOE-8 are being re-run owing to anomalies with the acid balance results.

Table 2 shows the high and low level for each of the tests, as well as two of the primary responses, namely vanadium recovery percentage and sulfuric acid

consumption. Highlighted areas correspond to the upper quartile of vanadium recovery, i.e. the top four tests. The highest vanadium recoveries are associated

with some combination of higher sulfuric acid dosage and temperature. The best four combinations average 91.7% vanadium recovery with the highest recovery of

94.3% associated with a low percentage of solid solution, and higher temperature and acid dosage. The upper quartile vanadium tests show acid consumptions

ranging between 88 kg/t and 142 kg/t with an average of 109 kg/t.

The high temperature runs consistently outperformed the low temperature runs with respect to vanadium. Acid dosages have a lower level of impact than

temperature on recovery. High solids density has a negative influence on the recovery, though not as statistically significant as temperature or sulfuric acid

dosage.

Phase II Testing Underway

Further testing is underway that will better define operating parameters required to develop an economic atmospheric leaching process. It should be noted that

the initial DOE runs are not optimized. Supplemental testing is in progress to augment the initial DOE with additional runs to optimize the leach parameters. It is

expected that improvements in recovery and acid consumption are likely.

Testing of several samples spatially distributed throughout the deposit and at different vanadium grades, will also be completed ("variability testing") to confirm

metallurgical responses throughout the deposit. Results of the variability testing will be used to develop the geometallurgical model for the Iron Point deposit and

support the engineering and design process. Additionally, bulk samples will be used to generate pregnant leach solution for subsequent solvent extraction and

vanadium precipitation testing. Owing to the nature of the Victory leach process, downstream processing of the vanadium rich solutions will be via a commercially

proven process to produce a high grade V

product.

Qualified Person

The scientific and technical information in this news release has been reviewed and approved by Jeffrey L. Woods, B.Sc., SME-QP, MMSA-QP, who is a

Qualified Person as defined by National Instrument 43-101.

About Victory Metals

Victory owns a 100% interest in the Iron Point Vanadium Project, located 22 miles east of

Winnemucca, Nevada

. The project is located within a few miles of

Interstate 80, has high voltage electric power lines running through the project area, and a railroad line passing across the northern property boundary. The

Company is well financed to advance the project through resource estimation and initial feasibility study work. Victory has a proven capital markets and mining

team led by Executive Chairman

Paul Matysek

. Major shareholders include Casino Gold (50%), and management, directors and founders (25%). Approximately

51% of the Company's issued and outstanding shares are subject to an escrow release over three years.

Please see the Company's website at

www.victorymetals.ca

On Behalf of the Board of Directors of

VICTORY METALS INC.

Paul Matysek

Executive Chairman and Director

Neither the TSX Venture Exchange nor its Regulation Services Provider (as that term is defined in the policies of the TSX Venture Exchange) accepts

responsibility for the adequacy or accuracy of this release.

Forward-Looking Information

This news release contains certain forward-looking information and forward-looking statements within the meaning of applicable securities legislation

(collectively "forward-looking statements"). Certain information contained herein constitutes "forward-looking information" under Canadian securities legislation.

Generally, forward-looking information can be identified by the use of forward-looking terminology such as "expects", "believes", "aims to", "plans to" or

"intends to" or variations of such words and phrases or statements that certain actions, events or results "will" occur. Forward-looking statements are based on

the opinions and estimates of management as of the date such statements are made and they are subject to known and unknown risks, uncertainties and other

factors that may cause the actual results, level of activity, performance or achievements of the Company to be materially different from those expressed by

such forward-looking statements or forward-looking information, including the business of the Company, the

speculative nature of mineral exploration and

development, fluctuating commodity prices, competitive risks, and

delay, inability to complete a financing or failure to receive regulatory approvals. Although

management of the Company has attempted to identify important factors that could cause actual results to differ materially from those contained in forward-

looking statements or forward-looking information, there may be other factors that cause results not to be as anticipated, estimated or intended. There can be

no assurance that such statements will prove to be accurate, as actual results and future events could differ materially from those anticipated in such

statements. Accordingly, readers should not place undue reliance on forward-looking statements and forward-looking information. The Company does not

undertake to update any forward-looking statements or forward-looking information that are incorporated by reference herein, except as required by applicable

securities laws.

View original content to download multimedia:

http://www.prnewswire.com/news-releases/victory-metals-demonstrates-over-90-vanadium-recovery-using-a-hydrometallurgical-leach-process-at-the-iron-point-project-nevada-300833504.html

SOURCE

Victory Metals Inc

View original content to download multimedia:

http://www.newswire.ca/en/releases/archive/April2019/17/c1407.html

%SEDAR: 00015775E

For further information:

contact Collin Kettell at [email protected] or (301) 744-8744.